Extruded Acrylic
Folded Label HolderBalustrade GlazingCanopy GlazingGlass Edge AcrylicPoint Of DisplayPolished EdgesStaircase Panel Glazing

You've Selected...

Extruded Acrylic

High quality extruded acrylic sheet ideal for a wide variety of industries, it offers excellent thickness tolerance and is extremely easy to vacuum form, making it ideal for applications where complex shapes are required.

Finishing & Fabrication Available

  • CNC Router
  • Drilling
  • Line Bend
  • Diamond Polishing
  • Flame Polishing
  • Edge Routing
  • CNC Laser
  • Saw Cutting
See options below

Applications

Signs, POS, glazing, displays, forming & fabrication.

Properties

  • Outstanding resistance to weathering
  • Excellent thermoforming capabilities
  • Good optical clarity
  • Full range of sheet sizes available for optimum economic usage
  • Hard wearing
  • Easily fabricated
  • High gloss finish

Technical Data

Fire Rating:
BS476 Part 7: Class 3

Light Transmission:
Clear 92% Opals (030) 70% (040) 51% (050) 37% (069) 9%

Co-efficient of Linear Expansion:
DIN 53752-A 1/K 7.10-2

Product Options

Sheet Size / Thickness (mm) 2mm 3mm 4mm 5mm 6mm 8mm 10mm
acrylic clear
2050 x 1520mm
2050 x 3050mm
2440 x 1220mm
acrylic opal 050
2030 x 1520mm
2030 x 3050mm
acrylic white 069
2050 x 1520mm
2050 x 3050mm
acrylic mirror
2050 x 3050mm
1220 x 2440mm
prismatic acrylic
2440 x 1220mm
acrylic antiglare
2050 x 3050mm

Technical Specifications

Property Test Method Conditions Units Value
Physical Extruded IM50 IM60
Relative Density ISO 1183 g/cm3 1.2 1.17 1.16
Water Absorption ISO 62 % 0.2 0.3 0.3
Mechanical
Tensile Strength at yield ISO 527 5mm/min MPa 70 68 50
Tensile Strength at break
Elongation at yield
Elongation at break ISO 527 5mm/min % 4 18 25
Tensile Modulus of Elasticity
Flexural Modulus ISO 178 2mm/min MPa 3030 2500 2000
Flexural Strength at yield ISO 178 2mm/min MPa 107 90 70
Izod Impact Strength ISO 180/1A notched kJm-2 N/A 5 7
Charpy Impact Strength ISO 179
ISO 179
unnotched
notched
kJm-2
kJm-2
10
N/A
50
5
65
7
Impact Falling Weight
Rockwell Hardness ISO 2039-2 M Scale 101 65 45
Thermal
Service Temperature °C -40 to 80
Heat Distortion Temperature
Vicat Softening Temperature ISO 306 °C >105 >105 >105
Coefficient of Thermal Expansion ASTM D-696 mm/m°C 0.078 N/A N/A
Thermal Conductivity
Specific Heat Capacity
Optical
Light Transmission ASTM D-1003 3mm sheet % >92 90 89
Refractive Index ISO 489/A 1.49 N/A N/A
Yellowness Index
Haze
Electrical
Dielectric Strength IEC 243 kV/mm-1 N/A N/A N/A
Surface Resistivity IEC 93 Ω m-2 >10
Flammability
Standard Classifcation
BS 476 Part 7 Class 4
UL 94 HB
NFP 92-307 M4 (without drips)

 

Acrylic is a combustible material and if ignited will continue to burn. Different to cast, extruded acrylic will eventually produce molten droplets which will continue to burn.

Other physical properties and values available on request.

"Thank you very much for your information package never mind your impressive client list and various services offered i was sold on the chocolate bar. On a serious note it is a very refreshing approach."
Danny
"We couldn’t ask for more from TBS Poly who are our new distributors in Cheshunt. Its important we give them every support in the first few months to help make it a success for them "
Richard
"When you’re working on a high profile job, you need to use the best quality products………… TBS polycarbonates are the company of choice…… thanks again guys!  "
Bert Hussein
"Friendly, knowledgeable and approachable with a guarantee of quality."
Catherine Thomas
"In an industry which can still be very male orientated, it is really nice to deal with a company who are always helpful, friendly, polite and above all patient, Tracey"
Tracey
"Always a good service from TBS"
John Monaghan
More great comments...