Solid Polycarbonate UV

Polycarbonate sheets deliver the transparency of glass at less than half the weight combining superior impact resistance and clarity, making it the material of choice for many demanding applications. Polycarbonate can be fabricated and formed, making it ideal for applications such as barrel vault roofing, roof lights and glazing. Clear, translucent or opaque polycarbonate sheets are also ideal for safety glazing applications, with excellent fire resistance. Another application is temporary glazing panels where polycarbonate is perfect due to its clarity, strength and how easy it is to cut to size with simple tools such as a jigsaw. TBS is an exclusive distributor and stockist in the UK of 15mm clear solid 2050mm x 3050mm polycarbonate sheet.

Finishing & Fabrication Available

  • CNC Router
  • Drilling
  • Cold Bend
  • Edge Routing
  • Saw Cutting
See options below


Security glazing, north lights, protective visors/guards, balustrades, fabrication.

Patterned & tints:
Security privacy glazing, balustrades and balconies, north lights, curtain walls.


  • Excellent fire resistance
  • UV protected on both faces
  • Extremely high impact resistance
  • High light transmission

Technical Data

Fire Rating:
BS476 Part 7: Class 1Y

Light Transmission:
Clear 88%, Bronze 50%, Opals 55%, 37% 25% (3mm)

Co-efficient of linear Expansion:
DIN 53752 10-6/°C 60-70

Anti Bandit Glazing

Safety glazing for use in buildings

Product Options

Sheet Size / Thickness (mm) 1mm 1.5mm 2mm 3mm 4mm 5mm 6mm 8mm 9.5mm 12mm 15mm
UV Clear Polycarbonate
2050 x 1250mm
2440 x 1220mm
2050 x 1523mm
3050 x 2050mm  •*
4050 x 2050mm
4500 x 2050mm
6050 x 2050mm
3050 x 2030mm
3050 x 2050mm
3050 x 2050mm
2440 x 1220mm
2050 x 1523mm
3050 x 2050mm
3000 x 2000mm
Prismatic Polycarbonate
2440 x 1220mm
Polycarbonate Antiglare
2050 x 3050mm


Technical Specifications

Property Test Method Conditions Units Values
Relative Density ASTM D-792 g/cm3 1.2
Water Absorption ASTM D-792 24hr @ 23°C % 0.15
Tensile Strength at yield ASTM D-638 10mm/min MPa 65
Tensile Strength at break ASTM D-638 10mm/min MPa 60
Elongation at yield ASTM D-638 10mm/min % 6
Elongation at break ASTM D-638 10mm/min % >90
Tensile Modulus of Elasticity ASTM D-638 1mm/min MPa 2,300
Flexural Modulus ASTM D-790 1.3mm/min MPa 2,600
Flexural Strength at yield ASTM D-790 1.3mm/min MPa 65
Izod Impact Strength ASTM D-256 notched J/m 800
Charpy Impact Strength ASTM D-256 notched J/m 800
Impact Falling Weight ISO 6603 3mm sheet J 158
Rockwell Hardness ASTM D-785 R Scale 125
Service Temperature °C -50 to +100
Heat Distortion Temperature ASTM D-648 Load: 1.82MP °C 130
Vicat Softening Temperature ASTM D-1525 Load: 1Kg °C 150
Coefficient of Thermal Expansion ASTM D-696 mm/m°C 0.065
Thermal Conductivity C-177 W/m°K 0.21
Specific Heat Capacity C-351 kJ/kg°K 1.26
Service Temperature ASTM D-1003 % 89
Refractive Index ASTM D-542 1.586
Yellowness Index ASTM D-1925 <1
Haze ASTM D-1003 % <0.5
Service Temperature ASTM D-149 500V/s kV/mm >30
Refractive Index ASTM D-257 Keithley Ω 5.1×10


Standard Classifcation
EN13501 B, s1, d0
BS 476 Part 7 Class 1
UL Classified V2 (File e221255)
NSP 92501,4 M2
DIN 4102 B1, B2
ASTM D-635 CC1


Other physical properties and values available on request.

"In an industry which can still be very male orientated, it is really nice to deal with a company who are always helpful, friendly, polite and above all patient, Tracey"
"You always seem to have what we need and are also prepared to go the extra mile"
Graham Green
"A very relaxed and happy company to deal with. Professional and always willing to help."
Sean Garwood, Manager
"Always a good service from TBS"
John Monaghan
"A friendly company who put customer service/satisfaction first"
Jayne Griffiths, Office Administrator
"Happy, vibrant work force ready and eager to help"
Jon Casey
More great comments...